КОМПЛЕКСНИЙ ПІДХІД ДО ОЦІНЮВАННЯ ЕФЕКТИВНОСТІ ВОГНЕЗАХИСТУ ІНТУМЕСЦЕНТНОГО ПОКРИТТЯ ДЛЯ ДЕРЕВИНИ
Анотація
COMPLEX APPROACH TO EVALUATION OF THE EFFICIENCY OF WOOD PROTECTION WITH INTUMESCENT COATING
Ju. Tsapko, А. Tsapko
Abstract. The complex approach to estimation of efficiency of application of intumescent coating for wood, the peculiarity of which is investigation of flame retardant efficiency of a covering, installation of fire-hazardous properties and research of operational characteristics, is offered. The solution of this problem is carried out according to standard methods. It is revealed that for rough wood there is a rapid process of combustion of material and the release of a significant amount of heat, for fire-proof wood the temperature is lower than the temperature of ignition of wood. In order to establish fire protection efficiency in the application of coatings, studies have been carried out on determining the group of wood burning in terms of mass loss and increase in temperature of flue gases, and it was established that when the coating is treated, the wood passes into a group of heavy materials. Experimental studies have established that after placing a sample of wood in the test chamber, its ignition begins with the release of a significant temperature and the spread of the flame on the surface; instead, for a sample of fire-retarded wood there is a gradual decrease in temperature, that is, the work of the coating is fixed, and accordingly, the decrease in the smoke-forming ability of the wood is flame retardant coating . It has been established that as a result of surface treatment with intuessent coating, products lose the ability to moisten and absorb water, which provides them with resistance to atmospheric factors and reduces the permeability of corrosion-resistant corrosion resistant sponge components several times.
Keywords: fire resistance, coating, wood, mass loss, charcoal, temperature, flame, surface treatment.
Посилання
Tsapko Ju. Evaluation of effectiveness of wood fire protection upon exposure to flame of magnesium /Ju. Tsapko, S. Guzii, M. Remenets, A. Kravchenko, О. Tsapko // Eastern-European Journal Enterprise Technologies. – 2016. – Vol. 4, № 10 (82). – P. 31–36.
Kryvenko P. Determination of the effect of fillers on the intumescent ability of the organic-inorganic coating of building constructions / P. Kryvenko, Ju. Tsapko, S. Guzii, A. Kravchenko // Eastern-European Journal of Enterprise Technologies. – 2016. – Vol. 5/10 (83). – P. 26–31.
Tsapko Ju. Simulation of the phase transformation front advancement during the swelling of fire retardant coatings / Ju. Tsapko, А. Tsapko // Eastern- European Journal Enterprise Technologies. – 2017. – Vol. 2, № 11 (86). – P. 50–55.
Tsapko Ju. Establishment of the mechanism and fireproof efficiency of wood treated with an impregnating solution and coatings /Ju. Tsapko, А. Tsapko Eastern- European Journal Enterprise Technologies. – 2017. – Vol. 3, № 10 (87). – P. 50–55.
Carosio F. Oriented Clay Nanopaper from Biobased Components Mechanisms for Superior Fire Protection Properties / F. Carosio, J. Kochumalayil, F. Cuttica, G. Camino, and L. Berglund // Washington: ACS Appl. Mater. Interfaces. – 2015. – 7 (10). – P. 5847–5856.
Dr. Simone Krüger. Neue Wege: Reaktive Brandschutzbeschichtungen für Extrembedingungen / Dr. Simone Krüger, Dr.-Ing. Gregor J. G. Gluth, Marie-Bernadette Watolla, Michael Morys, Dustin Häßler and Dr. Bernhard Schartel // Berlin, Bautechnik. – 2016. – Vol. 93, Issue 8. – P. 531–542.
Ciripi, В. К. Assessment of the thermal conductivity of intumescent coatings in fire / В. К. Ciripi, Y. C. Wang, B. Rogers // Fire Safety Journal. – 2016. – Vol. 81. – P. 74–84.
Завантаження
Опубліковано
Номер
Розділ
Ліцензія
Стосунки між правовласниками і користувачами регулюються на умовах ліцензії Creative Commons Із Зазначенням Авторства – Некомерційна – Поширення На Тих Самих Умовах 4.0 Міжнародна (CC BY-NC-SA 4.0):https://creativecommons.org/licenses/by-nc-sa/4.0/deed.uk
Автори, які публікуються у цьому журналі, погоджуються з наступними умовами:
- Автори залишають за собою право на авторство своєї роботи та передають журналу право першої публікації цієї роботи на умовах ліцензії Creative Commons Attribution License, котра дозволяє іншим особам вільно розповсюджувати опубліковану роботу з обов'язковим посиланням на авторів оригінальної роботи та першу публікацію роботи у цьому журналі.
- Автори мають право укладати самостійні додаткові угоди щодо неексклюзивного розповсюдження роботи у тому вигляді, в якому вона була опублікована цим журналом (наприклад, розміщувати роботу в електронному сховищі установи або публікувати у складі монографії), за умови збереження посилання на першу публікацію роботи у цьому журналі.
- Політика журналу дозволяє і заохочує розміщення авторами в мережі Інтернет (наприклад, у сховищах установ або на особистих веб-сайтах) рукопису роботи, як до подання цього рукопису до редакції, так і під час його редакційного опрацювання, оскільки це сприяє виникненню продуктивної наукової дискусії та позитивно позначається на оперативності та динаміці цитування опублікованої роботи (див.The Effect of Open Access).